We offer standard bars in a variety of diameters, from 3 mm to over 600 mm, cut to customer-specified thicknesses, lengths and surface finishes. We also offer precision machining, threaded bars and CNC, welded fabrication. As with all of our materials, our bars start as ingot magnesium ingots, sintered, then forged and drawn, extruded. Our advanced drawing/forging/casting/extrusion processes allow us to customize our products to meet specific customer material and performance requirements, ensuring optimum performance in your application.
MB8 Magnesium Bar Product Details:
1) Material grade MB8.
2) Near grade MA8 (Russia).
3)Technical standard of the material.
GB/T 5153-1985 《Processing magnesium and magnesium alloy grades and chemical composition》
GB/T 5154-1985 《Magnesium alloy plate》.
GB/T 5155-1985 《Hot Extruded Bars of Magnesium Alloy》.
GB/T 5156-1985 《Magnesium alloy hot extruded profiles》.
HB 5203-1982 《Hot Extruded Profiles of Magnesium Alloy for Aeronautical Use》.
HB 6690-1992 《Magnesium alloy forgings》.
4) Chemical composition. Chemical composition of the alloy according to GB/T 5153-1985
MB8
Mn (Manganese) 1.3 - 2.2;
Ce (Cerium) 0.15 - 0.35;
Mg (Magnesium) Rest;
Al (Aluminum) < 0.2;
Zn (Zinc) < 0.3;
Cu (Copper) < 0.05;
Ni (Nickel) < 0.007;
Si (Silicon) < 0.1;
Fe (Iron) < 0.05;
Be (beryllium) < 0.01;
Other elements < 0.3;
5) Heat treatment system.
A .F state, hot rolled, hot extruded or hot forged state.
B .O state cold rolled plate annealed 320 ~ 350 art, holding 0.5h.
C.Solid H112 state: semi-cold work hardening, 260 ~ 290 ℃, insulation 0.5h.
6) Specification and supply status.
standard |
variety |
state |
CB/T 5154-1985 |
Hot Rolled Plates |
F |
Cold Rolled Annealed Plates |
O |
Semi-Cold Hardened Plates |
H112 |
High quality plates for skinning |
O |
CB/T 5155-1985 |
Rods |
F |
GB/T 5156-1985 HB 5203-1982 |
Profiles |
F |
HB 6690-1982 |
Free forgings |
F |
Die forgings |
7) Application profile and special requirements.
The alloy has been mass-produced and is mainly used for aircraft skins, wall panels and parts for gasoline and lubricating oil systems.
Fully integrated magnesium rod manufacturing:
When the characteristics and properties of magnesium materials must be tightly controlled for superior end-product performance, companies rely on Maige's unparalleled expertise in magnesium alloys. Our advanced magnesium processing technology produces pure magnesium as well as specific metal alloys. By selectively influencing all aspects of the metallurgical process, we can alter properties such as porosity, strength and heat resistance to meet specific customer needs. At Maige, our process is fully integrated, starting with magnesium ingots, which are then made into semi-finished products through a range of advanced mixing, pressing, deforming and heating techniques. Finished products are then carefully manufactured to customer specifications utilizing our state-of-the-art processing and fabrication techniques. By controlling every step of the production process from ingot to finished product, we ensure that our products consistently deliver the performance and quality our customers demand.
Precision machining, fabrication and assembly:
Maige also offers precision magnesium machining and fabrication capabilities. We have honed our processes over decades of successfully handling magnesium. At our facility in China, Maige has over 40 machines dedicated to supporting your magnesium precision machining and fabrication needs. Customized Magnesium Weldments,Magnesium Alloy Part and Magnesium Alloy Vibrating Platforms can be provided to meet your needs.